一．适用：
牛仔布(涂层布，压光布除外)、硅油布、尼龙布、TPU、PU皮革等。
二．性能指标：
外观及组成：白色状粘稠体，聚氨酯聚合物
布氏粘度：120000~140000CPS
PH值：7.0±0.5
离子类型：阴离子
固体含量：50%±1
三．特性：
立体感强，高附着力，触边性好，透明性好，表面光滑。牢度超强、不粘手、高光泽、耐石磨洗、雪花洗、漂洗、酵素洗、酸洗、耐高温蒸煮。耐黄变.5-35℃常温下保存12个月，属于环保型胶浆。
四．操作应用：
1．本产品一般使用80目120目网布，根据图案的不同丝网一定要绷紧，这一点相当关键：
2．为了保证印制效果，一般不要制作太厚网版，根据厚度不同需要印5—8次，在使用厚网版印刷时印完第一次需待底层干透后再进行第二次印刷，一般印刷3—4次就能达到2-3毫米以上的高度。
3．本产品不易塞网，过稠时可加入适当水浆搅拌均匀进行稀释。
4．在自然风干48小时后，再过温150度8-15秒，过温时尽量将面料过反面。
5．如需提高牢度，使用时可加入1%-2%催化剂或交联剂。
Otherdetailedinformation
Brand
Conghui
Model
220
Viscosity
/℃
PH
℃
Odour
/
Stretch
100T
fineness
/um
appearance
Use
Colorstrength
100percent
Fluidity≥
/mm
expiration
12months
Singlenetweight
5KG
Resintype
/
Ionperformance
anion
Surfacecolor
一．Substrates
Uncoatedornon-presseddenim,siliconcoated,nylon,TPUorPUleather.
二.Indicatorsofperformance:
Appearanceandcomposition:whitedope,polyurethanepolymer
Brinellviscosity:120000～140000CPS
PH:7.0±0.5
Ionictype:anion
Solidcontent:50%±1
三.Productfeatures:
Highstackingproper,goodadhesionfastnesstofabrics,goodthixotropy,greattransparency,smoothfinish,superfastness,non-after tack,high glossiness,resistance to stone wash、snow wash、bleach、enzyme and acid wash.Resistance to high temperature steaming,yellowing.It can be stored at normal temperature of 5-35℃ for 12 months.It belongs to environmental paste.
四．Applicationofoperation
1.using80meshscreenand120meshscreen.Thekeypointisthescreenshouldbetightenedaccordingtodifferentpatterns.
2.Inordertoguaranteetheprintingeffect,donotmakethickaccordingtodifferentthicknessshouldbeprintedfivetoeighttimes.Whenusingthethickscreenprinting,youcanprintinthesecondtimeafterthebottomiscompletelydriedoffirsttime.Itcanreachmorethantwotothreemmheightwhenithasbeenprintedthreetofourtimesingeneral.
3.Thisproductiseasytoprintthroughfinemeshscreen,youcanaddappropriatewaterslurrytodilutewhentheitistoothick.
4.Afterthefortyeighthoursofnaturalairdry, and then over-temperature at 150℃ for 8-15 seconds.In the process of over-temperature,fabrics should be in opposite side as soon as possible.
5.Ifneedtoincreasethefastness,youcouldadd1-2% catalyst or cross-linker in usage.